Alu Bond

Panels Tone map Tree decor

Bond panels B2, B1, A2

Bond Composite Panels-represent a quality and long-term solution for the most demanding modern architecture and as such are the most common choice. In addition to its beautiful aesthetic appearance, a high-quality wrapper is also available that easily adjusts to designer designs and needs.

Bond Panels are excellent thermal insulators and reduce the cost of heating and cooling. The possibility of combining all colors from Ral cards and metallic colors. Bond Panels are dominant in relation to other materials in terms of processing, cutting, stitching and even 1.6 times lighter then aluminum and 3.4 times lighter then steel.

The panels can have a different type of fill. The most common fill is polyethylene PE as well as fireproof filling if the panels are used in the construction of special purpose objects. The panels used for outdoor use have sheet thicknesses of 0.4mm or 0.5mm and they have a PVDF coating that provides long-lasting protection and resistance to atmospheric influences. The panels intended for indoor use have sheet thickness of 0,3mm and 0,2mm. In order to make use of a larger percentage of the panels, we offer different dimensions.

Aluminum composite panels sold by our company are quality and carefully selected. Possession of certificates as well as guarantees on all our products provides security and guaranteed satisfaction to our current and future clients.

Rok isporuke A2 protivpožarnih panela od 2-3 nedelje,standardne širine,boje, dužina po izboru.

Technical Specification
Panel thickness	2mm	3mm	4mm
Thickness of aluminum sheet	0,21mm, 0,3mm	0,21mm, 0,3mm	0,3mm, 0,4mm, 0,5mm
Weight (kg/m²)	3.0 3.2	4.0 4.3	5.4 5.7 6.0
Tape strength at 180º	>5N/mm	>5N/mm
Fill (core)	PE	PE	LDPE

Dimensions of Tolerance
Thickness	± 0.2mm
Width	± 2mm
Length	± 3mm
Diagonal	± 5mm
Thermal expansion	2.4mm/m 100ºC temperature difference
Aluminum thickness	± 0.02mm
Thickness of coating (polyester)	poliester ≥ 16µm
Hardness	H
Strength	2T without cracking
Thermal resistance	-50ºC/+70ºC
Resistance to hot water	After 2 hours in hot water - no changes
Resistance to acids	24 hours after immersion in 5% by Hc1 - no surface changes
Resistance to alkalis	24 hours after submerging in 2% by NaOH - no surface changes
Resistance to the solvent base	In 100 cleaning cycles - there are no changes